HEP and HRSG INSPECTION and MAINTENANCE: Factor European experience into O&M practices at US combined cycles?

Posted on 21st Jul 2019

When we gather with colleagues, we listen closely for details and keep a notebook handy for those Rules of Thumb that transfer experience. We can also jot down a bulleted list of highlights, insights, and points of clarity. At a recent industry event in England, Consulting Editor Steve Stultz came away with a list of thought-provoking gems and a deeper sense of common global elements. They form the basis of his report, which follows.

Dr Ahmed Shibli, managing director, European Technology Development Ltd (ETD Consulting), organized and hosted a three-day International Conference on Power Plant Operation and Flexibility, preceded by two in-depth training courses. The July 2018 venue was the Institute of Materials, Minerals and Mining (IOM3) in central London.

The meeting covered recent developments in plant materials, operation, inspection, maintenance, and costs related to both baseload and cycling operation for different types of plants—including combined cycles, the focus here. Among the topics addressed in formal presentations and during discussion sessions were the following:                  

  • Equipment design, materials, and corrosion.

  • Operational constraints and optimization.

  • Component replacement, maintenance, and operating costs.

  • Strategies for optimizing inspection, maintenance, and cyclic operation.

  • Workforce, management, and automation issues.

Plant owners/operators were joined by researchers, manufacturers, and inspection-agency professionals.

A partial list of gems:

  • Europe is going through the same market changes as North America. Cycling is global.

  • Some countries have more cycling and low-load experience than North America—such as those with geothermal and hydroelectric plants that cause varied operation of fuel-fired assets. This experience base has wide-ranging value.

  • Europe and Japan are taking active roles in high-temperature materials development and testing.

Shibli’s primary purpose was to help identify the basic causes of equipment problems in both baseload and cycling plants, and to clarify modifications, inspections, and procedures that will minimize costs.

The ETD conference

Key themes were engineering design, materials R&D, new inspection techniques, cost analysis, and plant management/maintenance. Optional pre-conference training courses centered on operation and maintenance (Day One) and both short- and long-term system preservation (Day Two).

The agenda was divided into two parts. The first half discussed plant flexibility including new developments in creep-fatigue interaction in high-temperature plant materials. The second half focused on new developments in plant preservation, maintenance, inspection, monitoring, repair, and life assessment.

Selected highlights from the seven sessions are given below.

“Who wins when plant components fail?”

This question launched a presentation by David Allen (Impact PowerTech Ltd, UK) a consultant to ETD, on the upgrading of materials and welds. His next question was equally pointed: “Why do we so often stick with last-century technology?”

Allen first captured attention with a philosophical discussion of planned obsolescence. He cited interesting examples from the automobile, white goods, and communications industries. Participants were captivated, and on alert for more.

Allen did not claim current evidence of planned obsolescence within the power industry, and in fact stated that a manufacturer with a unique design is careful to maintain its good reputation.

But he did note some dangers similar to those expressed by Eskom (South Africa) at last year’s Air-Cooled Condenser Users Group meeting in Las Vegas.

We all experience the ongoing pressures for low bids, rapid investment payback, and increasingly stringent trading conditions. The potential menace is commonly applied standards that fail to ensure the most reliable long-term component operation.

In other words, once a supplier meets the standards or codes in the specification, further refinements or improvements can become less important (and more expensive) to the supplier. The same is true on qualifying bids for component supply. Providers’ reputations are at less risk as long as they meet the qualifications.

Perhaps because “innovation brings risk,” or because “regular repair and maintenance activities provide jobs,” we could be letting ourselves down, suggested Allen. And in his words, “We are still building new plants with 40-year-old materials (P91, Alloy 617) and ignoring the newer, potentially better alternatives.”

And how has market-driven flexible operation changed things? “Cycling makes it worse!”

Details have become clear, stressed Allen:

 • Mechanical and thermal fatigue cracking.

 • Creep-fatigue cracking (with creep ductility exhaustion attributed to repeated transient creep strain).

 • Creep cracking (with creep life reduction caused by increased loading).

So how do owners/operators minimize the potential costs? Allen outlined some thoughts:

1. Design out at-risk features” (thickness and materials mismatches, closely spaced header stubs, dissimilar-metal welds, etc).

2. Improve temperature control during startups and transients.

3. Make components thinner—perhaps.

Allen reviewed typical owner/operator options. Some choose to continue operation until plant end-of-life, mindful primarily of safety. Many take the financial hit and accept high inspection, repair, and replacement costs. The better strategy is to install upgraded retrofit components with stronger materials and welds at the same thickness (better for creep) or thinner (better for fatigue).

He then presented details and examples of current P92 materials (Fig 1) with good quality heat treatment, labeling this “a materials upgrade solution that is ready now.” Following in-depth discussions of various manufacturing methods, heats, ductility and tensile strength, he asked participants to “Stop fearing P92!” 

And he gave specifics from a recent review, showing a “strong correlation between heat treatment and ductility,” as shown in Fig 2. He concluded that “normalizing is about twice as important as tempering. Under-normalizing is the main problem. Under-tempering makes the problem worse.” And “notably, normalizing time is more important than temperature.”

Summary: This indicates that simple controls on allowable heat treatment can resolve the Grade 92 creep brittleness concern. Further work is ongoing to assess very long-term ductility out to 100,000 hours, and beyond.

Allen next looked at “near-future MarBN, a novel high-alloy steel for powerplants.” This material, being studied primarily in Japan and the UK, is martensite plus boron and nitrogen. The process involves “careful microalloying with boron and limited nitrogen for high creep strength.” Allen listed temperature capability of P92 as about 20 deg C better than P91 and “expects temperature capability of MarBN to be at least 25 deg C better than P92.”

But the microalloying process is extremely sensitive.

Following discussions on welding processes, he ended with the summary:

1. “Today we can replace P91 with P92.

2. Tomorrow we could use MarBN for even greater security.”

MarBN alloy

Zhuyao Zhang, Lincoln Electric Europe, followed with MarBN filler-metal development work from Impel and Impulse, two collaborative power-industry research programs in the UK. Intended applications include castings and forgings for steam-turbine components and steam piping (up to 650C). One slide included creep strength predictions (Fig 3).

His summary:

Aberrant P91 life predictions  

Shibli and David Robertson of ETD tag-teamed an in-depth presentation on life-prediction concerns for aberrant P91 components, often found in powerplants worldwide. They are usually the product of not understanding the precise heat-treatment requirements, by the component producers and fabricators, for high-Cr martensitic steels.

They issued a stark warning: “Traditional NDE techniques do not show damage in P91/P92 until late in life (70% or later), making current detection and component integrity management difficult.” New techniques are needed.

“A problem with 9Cr martensitic steels,” they said, “is that the creep cavity size for the first 70% of life can be on the nanometer or few-microns level only. Thus cavity detection and quantification by traditional means, such as replication or UT inspection, can be difficult.”

At the same time, “for aberrant microstructures powerplants often assume the safe life is equal to P22 or P91. But the industry could be underestimating life, thus condemning these components too early and thereby losing revenue. We currently do not have long-term rupture strength data for such abnormal microstructures to predict their safe operating life accurately.”

The two presenters gave examples of potentially abnormal materials:

Welding issues include:

Shibli outlined a six-year joint industry project that began in 2014 “aimed at producing 15 aberrant microstructures in P91 (both base and weld metals) and conducting stress rupture tests to 30,000 hours, which can then be extrapolated to 100,000 hours and beyond to estimate the safe operating life.”

Initial industry sponsors, coordinated by ETD, are various European and Japanese utilities, although new partners/sponsors are welcome at any stage to contribute towards the testing of one more of these aberrant microstructures. This project also involves detailed metallography, including use of transmission electron microscopes (TEM), to categorize the microstructures and their behaviors.

“To make matters worse and life assessment more difficult,” he continued, “it is now fairly well established that the creep failure stages for high-Cr martensitic steels (P91/P92) are reduced to creep cavity initiation, cavity growth, and failure with little warning.”

Specific visual examples were given for all points made in the presentation. Featured in the examples was Type IV damage in seam-welded components (Fig 4).

“The 9Cr martensitic steels have been very useful in raising powerplant temperatures and pressures (and making HRSGs more compact), improving plant output and efficiency,” Shibli stated. “However, more and more of these components are now showing cracking at the Type IV position associated with the weldments.”

And their conclusion: “Even components that can be identified to be at risk are creating issues for the plant owners and integrity assessors in view of the unknown long-term rupture strength of the aberrant steels, hence the need for the long-term stress rupture data to ensure their safe operation.”

More on materials

Other materials-related presentations included the cyclic loading and cyclic oxide conditions (Federal Institute of Materials Research & Testing, Germany), assessment of welds under creep, fatigue, and creep-fatigue loadings (University of Stuttgart, Germany), dissimilar metal welds in ultra-supercritical powerplants (Belgian Welding Institute), stress corrosion cracking in T24 material (VGB PowerTech Service GmbH, Germany), and microstructural evolution of P91 in high temperature conditions (INAIL, Italy).

HRSG revamp for GT upgrade

Pascal Fontaine, CMI Heat Recovery Systems (Seraing, Belgium), discussed example HRSG modifications to match a gas-turbine upgrade.

King’s Lynn Power Station in the UK is a high-efficiency, baseload combined cycle commissioned in 1996, designed for peak firing up to 370 MW. The plant is of Siemens single-shaft design with a 120-MW steam turbine and CMI vertical, triple-pressure, unfired HRSG.

The operating difficulty became inflexibility to market conditions. Thus, the unit was mothballed in 2012, but significant residual life remained in the plant infrastructure.

In 2016, owners signed contracts to revamp the plant and targeted more than 300 starts per year. The gas turbine and generator would be replaced, and the HRSG upgraded to match the new conditions, including new steam piping and attemperation systems. One street would be added to the air-cooled condenser.

Final superheater/reheater modules are now being replaced by two Euro Norm modules with additional heating surface.

Fontaine’s presentation walked systematically through the dismantling/replacement processes, including details of pipe-to-header welding and inlet duct restoration. 

King’s Lynn will return to commercial operation in 2019.

Cyclic-tolerant options

In a later conference session, Fontaine returned to discuss developments toward more cyclic-tolerant HRSGs—both horizontal and vertical designs.

A key part of this was the question: “What are the root causes of fatigue damage?”

He also discussed the benefits of internal accessibility for inspection and maintenance, offering examples for both horizontal and vertical designs.          

Fontaine ended with a discussion of superheater startup vents applied for multiple HRSGs on one steam turbine.

Thermal transient impacts

Richard Walton, SSE (formerly Scottish and Southern Energy Plc), addressed the group on thermal transients and their impacts throughout the SSE fleet, suggesting more targeted inspections, monthly monitoring and reporting, trending and investigating, and the need for improved industry guidance.

Details of his presentation outlined what he called “up-shock” and “down-shock” events and impacts on the HP and IP systems (superheater and reheater).

The benefits became recurring conference themes:

Change the inspection philosophy

James MacArthur, senior engineer, pressure systems, was also present from SSE and discussed the effect of UK grid demand on HRSG damage mechanisms. Running plants on demand is “arduous,” he stated, but one tactic is to “change the inspection philosophy.” 

His example was a 735-MW plant with two HRSGs, recently converted from baseload to two shifting, commissioned in the mid-1990s, and experiencing 900 starts in the past three years.

He reviewed fatigue-related damage locations: reheater tube stubs, reheater outlet and inlet headers, and superheater headers.

For the inlet header, a combination of system stresses and poor attemperation led to corrosion fatigue failure (a common topic). He also reviewed pipework stress analysis, indicating that “even with all supports operating correctly, stresses in the header stubs are high.”

Problems in his example case were caused by “anomalous and excessive axial stress during operation.” Stress analysis showed inadequate supporting and restraint arrangement on the outlet manifolds (Fig 5). “Even with all supports operating correctly,” he stated, “stresses in the header stubs were high.”

He then turned to both single- and two-phase FAC (flow-accelerated corrosion), pointing out locations, mechanisms, detection, and consequences. “In a combined-cycle plant,” he summarized, “FAC typically occurs in the LP and IP evaporator circuits, HP economizers, and feed pipework.” He pointed out that typical locations in conventional plants are the feedwater heaters and systems, and for all plants in air-cooled condensers.

This leads to the need (common theme again) of reassessing the inspection strategy as well as the impact of expected future operation (cycling).

Benchmarking, cycling analysis

Feroza Akther (ETD) reminded participants of the common impacts of cycling, including a note that owner/operators should also be aware of “higher fuel consumption during startups and shutdowns because of inefficient heat transfer and non-optimal heat rate.”

Therefore, owner/operators need to know the technical and financial impacts of converting base-load units to cycling, as well as the operating costs for current cycling units. Her presentation described both benchmarking and analysis for a large group of conventional and combined-cycle units.

The plant database included 30 conventional and 65 combined cycle units from Europe, US, and Asia, all with at least seven years of O&M data, ages from 1 to 35 years operation, and net generation from 50 to 500 MW. Analysis included data for:

Akther outlined ETD methodology of data analysis, statistical analysis and normalization (to share best practices), plant condition analysis to assess relevant O&M events, and how to determine O&M costs for equivalent hot starts. This included performance indicators (equivalent forced and planned outages, availability, and reliability) and annualized non-fuel costs.

“The performance assessment of the plants operating in cycling mode has been performed,” she said, “by demonstrating the evolution of forced and planned outage factors during the plant life cycle—that is, starting from commissioning until the end of plant life.” She labeled the phases as commissioning (one to six years), useful life (six to 20 years), and wear-out (more than 20 years).

Hot start is defined in this study as an overnight shutdown of less than eight hours, with turbine metal temperatures above 750F. Warm start reflects weekend shutdown of up to 60 hours (390F). Cold start is anything greater than 60 hours (below 390F).

Based on analysis of these units, “it appears that the strongest indicator of combined-cycle annual O&M costs is the number of equivalent hot starts (EHS) that the unit has performed.”

“To minimize economic impacts of cycling,” Akther explained, “it is crucial to create a well-balanced maintenance plan including proactive, predictive, and preventive programs.” This led to a discussion of advanced tools currently promoted including risk-based maintenance (RBM), condition-based maintenance (CBM), and reliability-centered maintenance (RCM).

Such programs are commonly discussed at these sessions. “If not already implemented,” stated Akther, “it will be extremely beneficial for the plants to consider these tools to achieve a well-balanced maintenance program.” Not surprising, perhaps, but reinforced.

Participant discussions were active and included a suggestion of adding the cost of lost generation to this study. An interesting follow-on discussion centered around the pros and cons of vertical versus horizontal HRSG designs.

Gen 3

ETD’s Nadeem Ahmed continued this theme with a look at a “Gen 3 RCM-based maintenance and reliability program.”

He began with a review of common programs and philosophies, listing the range of acronyms widespread throughout the industry.

“Gen 3,” he stated, “combines reliability and scheduled maintenance programs.” It focuses on reliability-centered maintenance, and “seeks the optimal mix of condition-based, time-based, and run-to-failure strategies.” He called it “a risk-based process for determining the least-cost maintenance and surveillance actions needed to meet operating performance targets.”

He then outlined implementation phases, including integration into plant operating and monitoring software.

Flexible operation studies

Uniper Energy Services’ Scott Lockyer discussed the company’s long-term flexible operation journey and offered thoughts on economic improvement from the operational view. Within this discussion was a process that seemed adaptable to various targeted component and system concerns.

The challenge was to minimize damage caused by cycling. The solution discussed:

The outcome: Implement modifications to operating procedures and/or design to address the identified issues.

Uniper has followed this process throughout its fleet for various at-risk areas including:

More on inspection

Other inspection topics included a boiler-tube inspection program for Southeast Asia’s first ultra-supercritical boiler (TNB, Malaysia), modeling of creep deformation and rupture criteria (Huddersfield Univ, UK), life assessment under creep-fatigue conditions (Univ of Stuttgart, Germany), high-temperature strain mapping in steel weldments using digital image correlation (Univ of Cape Town, South Africa), and DC/AC potential-drop technique for creep damage monitoring in piping systems (Metalect, UK).

Don’t forget the piping

Rob Wang, Engineering Analysis Services Ltd (UK), discussed outage planning and life extension of load cycling plants. He highlighted both piping system health management (Fig 6) and analytical techniques for component life assessment.

Piping system details are, perhaps, too often overlooked. Wang reminded participants of cyclic thermal movements, large stresses at nozzles, and incremental plastic collapse damage to constant-load hangers.

For system health issues, stated Wang, “long piping systems are subject to cyclic thermal movements that generate peak stress/strain at the nozzles and hangers.” Constant-load hangers (and variable-load spring supports) are used for balanced piping systems, allowing movement within clearly specified limits and maintaining stresses within code.

But operators must be aware of cycling’s impact, as well as the more common degradation forces of corrosion, loosening of bolted connections, and misalignments (among others). He therefore encouraged piping stress analysis and assessments, and periodic hanger surveys and full piping system reviews.

For the latter, he offered clear specifics:

Set up a live database from the design and installation records to include:

Conduct the following three surveys for every maintenance period:

For each survey, generate a technical report on findings, system health, and maintenance recommendations. He then gave details for each survey:

Pre-outage hot survey

Outage cold survey

Post-outage hot survey  

Wang stressed his recommendation to repeat these surveys for every maintenance cycle. He reminded participants to also inspect for any degradation by rust, lost or loose nuts, obstruction, misalignment, unintended deformation or configuration change, and to finish each survey process by informing outage planning of all findings.

Such information assists the entire plant in life-extension work, and provides early warnings on risk issues.

In the editor’s opinion, such level of detail is a hands-on and practical benefit to attending and participating in these sessions. The details reflect experience.

Drones expanded

Capitalizing on a development reported by Xcel Energy at previous HRSG Forums with Bob Anderson, Ahmed Shibli and William Moore issued an extensive report on ETD’s Group Sponsored Project on drones and robots for powerplant inspection.

The exploratory phase (just completed) of this project was directed at determining suitability of drones and robots for visual and UT inspection, as well as a review of R&D activities. The upcoming phase is the design and development of the most suitable and economic automated devices in three types:

1. Drones for visual inspection and data analysis of remote, out-of-view and at-height components.

2. Robots for polishing and UT inspection of components including crack sizing.

3. Small or mini-robotic devices for polishing and UT inspection requiring access through narrow spaces—such as between HRSG tubes.

4. Various organizations and experts are involved and more are invited to participate.

Drones. One development point is the oil and gas industry, currently using drones for UT inspection by attaching them to pipes. However, drones are not yet stable enough for complete UT inspection.

Some significant points were made:

In emergency shutdowns, a drone is a frontrunner for immediate access to the failure location. Quick access is especially beneficial if there is a need to procure materials or services. It also enhances the placing of scaffolding in the correct, precise location. Plus, drones can check surrounding areas before a chain of failures occurs and capture a permanent record.

For thermal surveys, drones are particularly adept at carrying thermal imaging cameras and reaching correct positions. This can identify the areas of heat leak or damage to insulation.

Powering the drones carries two options: internal combustion engines, or electrical power. Electric became the choice with lithium batteries, but carrying loads for long time periods is difficult. The group sponsored project is investigating this further.

Robots. For this project, a robot is defined as “a surface crawler that carries out visual/NDE inspection and sends inspection data to a remote-control unit.”

Robots can reach inaccessible areas, or those where scaffolding is required. There is a range of proven technologies for robots, robotic machines, and intelligent flexible arms, but further development is needed for the powerplant environment—for example, polishing heads and UT probes for wall-thickness measurements.

Current development recognizes the challenges. Robots are not suitable for climbing tubes with thick deposits. Closely-spaced wall tubes can limit access, and plants have wide variations in tube diameters and tube-to-tube gaps.

A look ahead. Robotic arm development, especially for access through narrow spaces, shows promise (Fig 7).

Stated Shibli, “a highly flexible and long robotic arm of about 0.4 in. diameter is needed that can pass between tubes in an HRSG, has multiple axes of rotation, and can carry out visual examination, surface polishing, initial inspection, and assessment.”

The next phase of this ongoing group sponsored project is development of “a novel drone-robot hybrid device.”

Other inspection techniques discussed included Obikou, a pipe strengthening mechanism for creep damage and/or steam welded pipes (ETD); a portable scanning force microscope (Fig 8) for early stage creep and fatigue damage detection and life assessment (ETD); electrical discharge sampling equipment for removal of samples from pressure vessels and turbine rotors for quality checks and life/crack assessment (ETD/SGS, UK); portable magnetic measurement equipment for onsite creep damage detection (Univ of Manchester, UK); and shop welding interruptions of P91 components (PPC, Greece).

Related topics

Related topics discussed at this comprehensive event included gas turbines coupled with upcoming battery technology (Engie Laborelec, Belgium); condenser failure modes and powerplant chemical cleaning (Bill Moore, consultant, UK), and fracture mechanics assessment for boiling-water-reactor circulating-pump bowls (TUV SUD Industrie Service GmbH, Germany).

The host

ETD’s various capabilities are described at www.etd-consulting.com. Emphasis is on high-temperature plant inspections and materials (P91 and others), component safety and durability, performance of in-service welds, and probabilistic life and crack assessment.

A conference similar to the one described in this article was organized by ETD Consulting and held in Charlotte, NC, in November 2012. Upcoming conferences will be announced in CCJ.

Above Selected Article is linked from below Website:

http://www.ccj-online.com/ccj-issue-58/hep-and-hrsg-inspection-and-maintenance-factor-european-experience-into-om-practices-at-us-combined-cycles/